Traditional, soft coatings, a technique commonly used for coating optical components, may soon be rendered obsolete by a higher performing coating technique known as hard coating. As detailed, hard coatings provide several advantages to traditional soft coatings.

 

Soft Coatings

Soft coatings are multilayer thin films consisting of zinc sulfide, cryolyte, and, sometimes, silver. For traditional interference filters, the coated components are laminated together in a vertical stack to provide some protection from the environment and, typically, cored from a larger wafer. Because of the materials and manufacturing process used, soft coatings are fragile. The coating material is often removed from the edges of the filter in order to avoid degradation caused by moisture and to increase the coating’s lifetime. A diagram of the finished product is shown in Figure 1.

Figure 1: Schematic of a traditional interference filter with a thin film coating

 

The cost of soft coatings is maintained by the low cost of the deposition equipment, fast cycle times, and inexpensive float glass substrates, but there are high handling costs due to the sealing and ring assemblies. The cost vs. volume ratio behaves with an asymptotic trend: expensive at low volumes and stabilizing only after a few dozen 1" pieces or a handful of 2" or larger pieces are created.

 

Hard Coatings

Hard coated films are developed using a plasma deposition process that provides multiple benefits compared to soft coatings. The plasma deposition process is tightly controlled using a computer, which allows for even layering, high environmental aptitude, and improved performance. For instance, not only is the transmittance of a hard coating more consistent as a function of wavelength, but it is also generally superior to the transmittance of a soft coating.

 

As shown in Figure 2, hard coatings can provide over 90% transmission throughout the visible spectrum and into the UV. On the other hand, soft coatings cannot achieve 90% transmission and face significant performance declines near the UV. Additionally, there are improvements with cut-on and cut-off transitions. Soft coatings have a gradual change from no transmittance to maximum transmittance, while hard coatings achieve much steeper transition.

Figure 2: Performance Comparison of Soft and Hard Coatings

 

Comparing the Performance of the Soft and Hard Coating Techniques

Attribute

Soft Coating

Hard Coating

Notes

Lifetime

1 to 5 years

Indefiniy (under normal operating conditions)

Soft coatings are more susceptible to environmental factors, especially high humidity. These lifetimes are considered in a typical office environment.

Temperature Stability

Averages 50 parts per million per wavelength

Less than 5 parts per million per wavelength

Soft coatings require a temperature control of ±15°C for a 1nm filter tolerance. Hard coatings can achieve less than 1 pm/°C at 1550nm much less than 1ppm/λ.

Manufacturing Repeatability

Low

High

Compley automated processes in hard coating production allows for increased repeatability.

Transmitted Wavefront Error

Can achieve less than λ/4 PV value

Can achieve less than λ/4 PV value

Hard coatings essentially have TWE values that equal the uncoated optic. Soft coatings have to go through extensive polishing after the lamination process.

Cost of production

Flattens out if a large volume is made

Low due to repeatability and automated process

It is possible for hard coatings to be sold in volume at the same or lower price than their soft coating counterpart.

Table 1: Benefit Comparison of Soft and Hard Coatings

联系我们

地址:江苏省江阴市人民东路1091号1017室 传真:0510-68836817 Email:sales@rympo.com
24小时在线客服,为您服务!

版权所有 © 2024 江阴韵翔光电技术有限公司 备案号:苏ICP备16003332号-1 技术支持:化工仪器网 管理登陆 GoogleSitemap

在线咨询
QQ客服
QQ:17041053
电话咨询
0510-68836815
关注微信